材质 |
用途 |
化学成分 |
力学能力 |
线径（mm） |
净重(kg) |
阀芯直径(mm) |
备注 |
|
ER304 |
主要用于焊接18Cr-8Ni钢 |
C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%
|
拉伸强度Mpa 1200 |
0.08-0.45 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER304L |
主要用于焊接17Cr-8Ni钢 |
C:0.028% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%
|
拉伸强度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER308 |
主要用于焊接19Cr-9Ni钢 |
C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10% |
拉伸强度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER308L |
主要用于焊接20Cr-9Ni钢 |
C:0.024% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%
|
拉伸强度Mpa 1200 |
0.8-4.5 |
5/12.5/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER309 |
主要用于焊接20Cr-13Ni钢 |
C:0.064% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10% |
拉伸强度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER309L |
主要用于焊接20Cr-14Ni钢 |
C:0.024% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%
|
拉伸强度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER309Lsi |
主要用于焊接20Cr-14Ni钢 |
C:0.024% Mn:1.65% Si:1.02% Ni:14.33% Cr:20.10% |
拉伸强度Mpa1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER321 |
主要用于焊接16Cr-7Ni钢 |
C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%Ti0.73 |
拉伸强度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER347 |
主要用于焊接16Cr-9Ni钢 |
C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% （Ta+Nb）（10*C）-10 |
拉伸强度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 0 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER347L |
主要用于焊接17Cr-9Ni钢 |
C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% （Ta+Nb）（10*C）-10 |
拉伸强度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 0 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER316 |
主要用于焊接16Cr-9Ni钢 |
C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03 |
拉伸强度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER316L |
主要用于焊接17Cr-9Ni钢 |
C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03 |
拉伸强度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER310 |
主要用于焊接24Cr-19Ni钢 |
C:0.064% Mn:1.65% Si:0.42% Ni:20.33% Cr:25.10% |
拉伸强度Mpa 1200 |
0. |